Microwave dielectric properties of Ti-substituted Bi2 (Zn 2/3Nb4/3)O7 pyrochlores at cryogenic temperatures
Journal Publication ResearchOnline@JCUAbstract
Monoclinic pyrochlore ceramic Bi2Zn2/3−x/3Nb4/3−2x/3TixO7 (M–BZN) with x=0–0.4 is synthesized and the structure and microwave cryogenic properties are scrutinized. The dielectric constant (ɛ') and loss tangent (tanδ) of these ceramics are measured at a frequency of 3 GHz and temperature range of 15–300 K. With an increase in x value from 0 to 0.4, the dielectric constant and dielectric loss tangent of the investigated materials increase from 70 to 114 and 0.009 to 0.061, respectively. The Ti-substituted ceramics show an increase in dielectric constant with temperature, and the loss tangent shows a peak around 200 K. The peak in the dielectric loss tangent becomes more prominent with an increase of Ti content. The temperature where the dielectric loss tangent peak appears is found to be decreasing slightly with an increase of titanium doping. The observed dielectric characteristics of the titanium-doped M–BZN ceramics are attributed to the presence of the relaxation in these materials, originating from the disorder caused by the Ti4+ substitution.
Journal
N/A
Publication Name
N/A
Volume
92
ISBN/ISSN
1551-2916
Edition
N/A
Issue
6
Pages Count
4
Location
N/A
Publisher
American Ceramic Society
Publisher Url
N/A
Publisher Location
N/A
Publish Date
N/A
Url
N/A
Date
N/A
EISSN
N/A
DOI
10.1111/j.1551-2916.2009.03025.x